| 布氏硬度 HB | 洛氏硬度 | 维氏 硬度 HV | 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | ||
| Hra | Haqniti | Hra | Haqniti | ||||
| 86.6 | 70.0 | 1037 | 78.5 | 55.0 | 599 | ||
| 86.3 | 69.5 | 1017 | 78.2 | 54.5 | 589 | ||
| 86.1 | 69.0 | 997 | 77.9 | 54.0 | 579 | ||
| 85.8 | 68.5 | 978 | 77.7 | 53.5 | 570 | ||
| 85.5 | 68.0 | 959 | 77.4 | 53.0 | 561 | ||
| 85.2 | 67.5 | 941 | 77.1 | 52.5 | 551 | ||
| 85.0 | 67.0 | 923 | 76.9 | 52.0 | 543 | ||
| 84.7 | 66.5 | 906 | 76.6 | 51.5 | 534 | ||
| 84.4 | 66.0 | 889 | 501 | 76.3 | 51.0 | 525 | |
| 84.1 | 65.5 | 872 | 494 | 76.1 | 50.5 | 517 | |
| 83.9 | 65.0 | 856 | 488 | 75.8 | 50.0 | 509 | |
| 83.6 | 64.5 | 840 | 481 | 75.5 | 49.5 | 501 | |
| 83.3 | 64.0 | 825 | 474 | 75.3 | 49.0 | 493 | |
| 83.1 | 63.5 | 810 | 468 | 75.0 | 48.5 | 485 | |
| 82.8 | 63.0 | 795 | 461 | 74.7 | 48.0 | 478 | |
| 82.5 | 62.5 | 780 | 455 | 74.5 | 47.5 | 470 | |
| 82.2 | 62.0 | 766 | 449 | 74.2 | 47.0 | 463 | |
| 82.0 | 61.5 | 752 | 442 | 73.9 | 46.5 | 456 | |
| 81.7 | 61.0 | 739 | 436 | 73.7 | 46.0 | 449 | |
| 81.4 | 60.5 | 726 | 430 | 73.4 | 45.5 | 443 | |
| 81.2 | 60.0 | 713 | 424 | 73.2 | 45.0 | 436 | |
| 80.9 | 59.5 | 700 | 418 | 72.9 | 44.5 | 429 | |
| 80.6 | 59.0 | 688 | 413 | 72.6 | 44.0 | 423 | |
| 80.3 | 58.5 | 676 | 407 | 72.4 | 43.5 | 417 | |
| 80.1 | 58.0 | 664 | 401 | 72.1 | 43.0 | 411 | |
| 79.8 | 57.5 | 653 | 396 | 71.8 | 42.5 | 405 | |
| 79.5 | 57.0 | 642 | 391 | 71.6 | 42.0 | 399 | |
| 79.3 | 56.5 | 631 | 385 | 71.3 | 41.5 | 393 | |
| 79.0 | 56.0 | 620 | 380 | 71.1 | 41.0 | 388 | |
| 78.7 | 55.5 | 609 | 375 | 70.8 | 40.5 | 382 | |
Davamlı metal materiallar sərtlik dəyəri çevirmə cədvəli
| 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | ||
| Hra | Haqniti | Hra | Haqniti | ||||
| 370 | 70.5 | 40.0 | 377 | 269 | 28.0 | 274 | |
| 365 | 70.3 | 39.5 | 372 | 266 | 27.5 | 271 | |
| 360 | 70.0 | 39.0 | 367 | 263 | 27.0 | 268 | |
| 355 | 38.5 | 362 | 260 | 26.5 | 264 | ||
| 350 | 38.0 | 351 | 257 | 26.0 | 261 | ||
| 345 | 37.5 | 352 | 254 | 25.5 | 258 | ||
| 341 | 37.0 | 347 | 251 | 25.0 | 255 | ||
| 336 | 36.5 | 342 | 248 | 24.5 | 252 | ||
| 332 | 36.0 | 338 | 245 | 24.0 | 249 | ||
| 327 | 35.5 | 333 | 242 | 23.5 | 246 | ||
| 323 | 35.0 | 329 | 240 | 23.0 | 243 | ||
| 318 | 34.5 | 324 | 237 | 22.5 | 240 | ||
| 314 | 34.0 | 320 | 234 | 22.0 | 237 | ||
| 310 | 33.5 | 316 | 232 | 21.5 | 234 | ||
| 306 | 33.0 | 312 | 229 | 21.0 | 231 | ||
| 302 | 32.5 | 308 | 227 | 20.5 | 229 | ||
| 298 | 32.0 | 304 | 225 | 20.0 | 226 | ||
| 294 | 31.5 | 300 | 222 | 19.5 | 223 | ||
| 291 | 31.0 | 296 | 220 | 19.0 | 221 | ||
| 287 | 30.5 | 292 | 218 | 18.5 | 218 | ||
| 283 | 30.0 | 289 | 216 | 18.0 | 216 | ||
| 280 | 29.5 | 285 | 214 | 17.5 | 214 | ||
| 276 | 29.0 | 281 | 211 | 17.0 | 211 | ||
| 273 | 28.5 | 278 | |||||
Qeyd:
1. Brinell Hardness: Əsasən tökmə, bağışlayan, əlvan metal hissələri, isti yayılmış zərdab və şişkin hissələrin sərtliyini ölçmək üçün istifadə olunur. Ölçmə diapazonu ≥hb450-dir.
2. Rockwell Sərtliyi: HRA, Sementlənmiş karbid, nitred polad və s. Kimi HRC67-dən daha yüksək olan materialların və səthlərin səth sərtliyini ölçmək üçün yüksək sərtlik üçün istifadə olunur. HRC, əsasən polad hissələrin sərtliyini (karbon polad, alət polad, yüngül polad və s.) Söndürüldükdən və ya temperingdən sonra ölçmək üçün istifadə olunur. Ölçmə diapazonu HRC20 ~ 67-dir.
3. Vickers Hardness: İncə hissələrin sərtliyini və polad nömrəli hissələrin sərtliyini ölçmək üçün istifadə olunur və karbürizləmə, sianid və nitriding kimi səth sərt hissələrinin sərtliyini ölçmək üçün də istifadə edilə bilər.
Time vaxt: Apr-07-2024